属于掺杂陶瓷材料的制备领域的彩色氧化锆陶瓷的制备方法。该方法按８５０－９８０份氧化锆粉体、１０－５０份稳定剂和１０－１２０份着色剂的配比，将稳定剂和着色剂加入到氧化锆粉体的悬浊液中，通过控制溶液的ｐＨ值或使用各种沉淀剂，使稳定剂和着色剂沉淀在氧化锆粉体的表面。
溶液经过滤后干燥，将得到的粉体进行研磨，过筛，然后经成型、脱脂和烧结得到彩色氧化锆陶瓷。本发明在纳米尺度上，实现了稳定剂、着色剂与纳米氧化锆粉体的均匀复合，能大量减少着色剂在氧化锆陶瓷高温烧结阶段的挥发，样品成色均匀，重复性好。
本方法制备的彩色氧化锆陶瓷可广泛应用于工艺装饰、钟表、刀具、手机外壳、珠宝首饰等领域。（图/文www.yxwdcy.com）
中译英：
Doped ceramic material belongs to the field of preparation of color zirconia ceramic preparation method. The method according to the 850 - 980 copies of zirconia powder, 10 - 50 and 10 - 120 colorant stabilizer formulation, will the stabilizer and colorant is added to the powder of Zirconia Suspension, by controlling the pH value of the solution or the use of a variety of precipitating agent, stabilizer and a colorant precipitate in zirconia powder surface.

Solution after filtration by drying, the powder for grinding, sieving, then forming, degreasing and sintering to obtain color zirconia ceramic. The invention in the nanometer scale, realized the stabilizer, coloring agent and nano zirconia powder homogeneous composite, can reduce the number of colorant in zirconia ceramics sintered at high temperature phase of the volatile, sample fineness uniformity, good repeatability.